Hard Cladding MAG Material / Welding Wire DW-H700
Codice componente
Qui sono indicati i codici componente
correlati al prodotto ricercato
DW-H700-1.2-20
Informazioni di base
| Product Type | Filo per saldatura | Wire Diameter(mm) | 1.2 | JIS Standard | Z3326 YF3B-C-600 |
|---|---|---|---|---|---|
| Amount Of Content | 1 winding (20 kg) | Mass(g) | 20000 | Application and Usage Characteristic | Suitable for anti earth and sand abrasion. Even after heat treatment, Mo, V, and W remain stable and the reduction in hardness is negligible. So it remains stable. |
| Chemical Composition of Deposited Metal B(%) | - | Chemical Composition of Deposited Metal C(%) | 0.57 | Chemical Composition of Deposited Metal Si(%) | 0.73 |
| Chemical Composition of Deposited Metal Mn(%) | 1.05 | Chemical Composition of Deposited Metal Cr(%) | 5.40 | Chemical Composition of Deposited Metal Mo(%) | 1.01 |
| Chemical Composition of Deposited Metal, Other | W:1.21 V:0.54 | Example of Weld Metal Hardness (Vickers Hardness) Welded State | 673 | Example of Weld Metal Hardness (Vickers Hardness) After Heat Treatment | 605 600℃×2h |
| Recommended preheating temperature and temperature between paths | 250 °C or More | Shield Gas | CO2 |
Configura
Proprietà di base
-
Tipo
- DW-H700
Filtrare per giorni di spedizione standard
-
- Tutti gli articoli
- 8 giorni o meno
Attributi opzionali
- Specifiche e dimensioni di alcuni componenti potrebbero non essere illustrate in modo esauriente. Per i dettagli esatti, consultare i cataloghi dei produttori .
Supporto tecnico
Metodo di pagamento
Produzione on demand
Certificati
Copyright © MISUMI Corporation All Rights Reserved.