MAG Material / Flux-Cored Wire for Soft Steel to 550 MPa Grade Steel DW-316L

Codice componente

Qui sono indicati i codici componente
correlati al prodotto ricercato

DW-316L-1.2-12.5

Codice componente
DW-316L-1.2-12.5
Codice componente
Prezzo unitario standard
Quantità minima d'ordineSconto volumi elevati
Giorni
spedizione standard
?

440.66 €

1 7 giorni

Loading...

  1. 1

Informazioni di base

Product Type Filo per saldatura Wire Diameter(mm) 1.2 JIS Standard Z3323 TS316L-FB0
AWS Standard A5.22 E316LT0-1,E316LT0-4 Amount Of Content 1 Box (12.5 kg) Mass(g) 12500
Application and Usage Characteristic Welding of low carbon 18% Cr - 12% Mo steel (SUS 316 L etc). An adequate amount of ferrite in the structure provides low cracking susceptibility and excellent weldability. Excellent corrosion resistance to dilute sulfuric acid. Chemical Composition of Deposited Metal C(%) 0.026 Chemical Composition of Deposited Metal Si(%) 0.59
Chemical Composition of Deposited Metal Mn(%) 1.43 Chemical Composition of Deposited Metal Mo(%) 2.34 Chemical Composition of Deposited Metal P(%) 0.02
Chemical Composition of Deposited Metal S(%) 0.010 Ni(%) 12.02 Cr(%) 18.95
Example of Weld Metal Mechanical Properties 0.2% Proof Stress MPa 380 Mechanical Properties of Weld Metal Proof Stress, Tensile Strength MPa 540 Mechanical Properties of Weld Metal Proof Stress, Elongation(%) 40
Mechanical Properties of Weld Metal Proof Stress, Absorption Energy(J) 44 Shield Gas CO2 Authorized by the Classification Society of Japan NK,ABS,LR,DNV,BV,GL